Low cycle fatigue (LCF) is low-cycle endurance testing, where components are subject to mechanical cyclic plastic strains that cause fatigue failure within a short number of cycles. °ÄÃÅ2023È«ÄêÕý°æÃâ·Ñ×ÊÁÏ provides testing to several industry specifications including ASTM E606, the standard test method for strain-controlled fatigue testing.
Fatigue testing can predict how a material will wear and react throughout its life, or in a high-stress environment. Low cycle fatigue is useful for simulating specific scenarios and investigating real-world failures.
What is the difference between HCF and LCF fatigue?
High cycle fatigue (HCF) uses a low force load over a large number of cycles to cause failure. This generates an SN (stress/number of cycles) curve, which predicts how it will wear over time. In contrast, low cycle fatigue (LCF) uses high levels of force over a smaller number of cycles to stimulate a high-stress environment that might cause a more immediate break. This is measures with a strain vs. life curve.
Low cycle fatigue (LCF) test procedure per ASTM E606
Before testing, the subject material is first machined and longitudinally polished or ground into cylindrical or flat test specimens with a uniform-gage section. The samples are then loaded into a tension-compression endurance testing machine and subject to repeated stress under a constant strain rate in accordance with ASTM E606. Extensometers are used to control strain range by measuring deformation in the gage section of the specimen.
Typical low cycle fatigue tests are targeted to run no more than 100,000 cycles. Test frequency ranges between 0.25 Hz and 5 Hz, depending on material and requirements.
By testing multiple specimens at varying strain levels, S/N or strain-life curves can be developed for the material. ASTM E606 recommends testing at least ten samples to gain statistical confidence in strain-life curves.
Fast, accurate LCF testing to a wide range of standards
°ÄÃÅ2023È«ÄêÕý°æÃâ·Ñ×ÊÁÏ offers LCF testing to a range of standards, including:
ASTM International
- ASTM E467, ASTM 606
British Standards
- BS 7270
General Motors Specifications
- GMW16704, GMW16705
International Organization for Standardization
- ISO 12106
Why choose °ÄÃÅ2023È«ÄêÕý°æÃâ·Ñ×ÊÁÏ?
At °ÄÃÅ2023È«ÄêÕý°æÃâ·Ñ×ÊÁÏ, we can perform a range of fatigue tests, including ASTM E466 high cycle fatigue, ASTM E606 low cycle fatigue, ASTM E2368 thermo mechanical fatigue (TMF) testing, and specialized programs on a range of metals and alloys, polymers, components, and medical applications.
°ÄÃÅ2023È«ÄêÕý°æÃâ·Ñ×ÊÁÏ has the unique capabilities required to provide comprehensive low cycle fatigue testing and results, from raw material blanking and specimen machining to precision data acquisition and reliable, comprehensive test reports.
For more information about our low cycle fatigue (LCF) testing or to request a quote, contact us today.
Ready to request a quote?
Our deliverable is certainty - high quality data, test reports and certificates that you can absolutely rely on when making decisions about your materials and compliance. Engage with an expert today.
Fatigue Failure: How can you Tell?Â
Fatigue failure is an extremely important design consideration for a variety of industries. Learn more about the characteristics of fatigue failure.
READ MOREA Guide to Fatigue Testing in Composite MaterialsÂ
We explain how composite fatigue testing is performed, key methods, how fatigue testing of impact-damaged laminates work, and fatigue crack growth testing.
READ MOREMultiaxial Fatigue Analysis
Multiaxial fatigue analysis replicates real-world service environments' load and stress conditions in controlled laboratory settings to develop safer materials and components.
Read moreRelated Services
![High Cycle Fatigue 640x480](/-/media/images/services/materials-testing/fatigue-testing-hcf-640x480.jpg?h=205&w=278&la=en&hash=FE2E70FD1909B4ED77FA0D7279A8A27F)
ASTM E466 High Cycle Fatigue (HCF)
High cycle fatigue is used for materials that experience low applied forces and where deformation is primarily elastic in nature.
![Thermomechanical Fatigue 640x480](/-/media/images/services/materials-testing/fatigue-testing-tmf-640x480.jpg?h=205&w=278&la=en&hash=71E329D46510251FD88F1011A0506BB1)
ASTM E2368 Thermo Mechanical Fatigue (TMF)
°ÄÃÅ2023È«ÄêÕý°æÃâ·Ñ×ÊÁÏ's ASTM E2368 thermo mechanical fatigue program provides testing services for a variety of materials qualification programs.
![Bending Fatigue Testing](/-/media/images/services/materials-testing/bending-fatigue-testing-640x480.jpg?h=205&w=278&la=en&hash=288C641A259B3C045B5A52092DDD59CF)
Fatigue Testing
Find out how °ÄÃÅ2023È«ÄêÕý°æÃâ·Ñ×ÊÁÏ's fatigue testing labs help companies meet quality requirements and create safer, stronger, more successful parts and products.
![Fatigue Crack Growth Testing](/-/media/images/services/materials-testing/fatigue-crack-growth-testing-640x480.jpg?h=205&w=278&la=en&hash=5F7F7F7ECD077BD5351F50DAC51DBFFA)
Fracture Toughness Testing
°ÄÃÅ2023È«ÄêÕý°æÃâ·Ñ×ÊÁÏ provides fracture toughness testing for determining material characteristics and longevity of metallic, nonmetallic, and advanced materials.